High Deposition Rate of Dual-cathode DC Unbalanced Magnetron Sputtering
- 1 Industrial Electrical Technology Program, Faculty of Industrial Technology, Valaya Alongkorn Rajabhat University under the Royal Patronage, Pathumthani 13180, Thailand
- 2 Physics Program, Faculty of Science and Technology, Phranakhon Rajabhat University, Bangkok 10220, Thailand
Abstract
Dual-cathode dc unbalanced magnetron sputtering for the deposition of ternary compound films with a high deposition rate was designed and constructed. It consists of two magnetrons of opposite magnetic polarities. Each magnetron consists of central and outer ring magnets with the residual inductions of 500 and 600 mT, respectively. The testing results of the system showed that high plasma volume could be created at a long substrate distance of about 15 cm from the targets. In addition, by using this sputtering system for coating TiAlN film, the result showed that at a target to substrate distance of 13 cm the film growth rate was 7.3 nm/min. It indicates that the sputtering system developed in this study is suitable for large substrate area coating due to the long distance of target to substrate.
DOI: https://doi.org/10.3844/ajassp.2020.231.239
Copyright: © 2020 Theeranon Chaiyakun, Wuttichai Phae-Ngam and Jedsada Prathumsit. This is an open access article distributed under the terms of the
Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
- 3,344 Views
- 2,376 Downloads
- 4 Citations
Download
Keywords
- Unbalanced Magnetron
- DC Magnetron Sputtering
- Dual Cathode